Mechanical Analysis of SAE 1018 SAE 1020 Steel Pipes

 

Chemical Resistance Guide SAE 1018 Steel Pipes

Grade C Mn Fe P S
AISI 1018 0.14 – 0.20 % 0.60 – 0.90 % 98.81 – 99.26 % ≤ 0.040 % ≤ 0.050 %
AISI 1020 0.170 – 0.230 0.300 – 0.600 99.08 – 99.53 ≤ 0.040 ≤ 0.050

 

AISI 1020 Seamless Pipe Mechanical Analysis

Grade Tensile Strength Yield Strength Elongation
AISI 1018 440 MPa, 63800 psi 370 MPa, 53700 psi 15.0 %
AISI 1020 380 MPa, 55100 psi 165 MPa, psi 29700 25 %

AISI 1020 alloy steel pipe can be largely utilized in all industrial sectors in order to enhance weldability or machinability properties. It is used in a variety of applications due to its cold drawn or turned and polished finish property. Due to its low carbon content, it is resistant to induction hardening or flame hardening.

 

AISI 1020 alloy steel pipe Specification

Outer Diameter: 40 – 245 mm

Thickness: 3 – 20 mm

AISI 1020 alloy steel pipe Chemical composition(%)

C:0.17-0.230 Fe:99.08-99.53 Mn:0.30-0.60 P≤0.040 S≤0.050

AISI 1020 carbon steel pipe Mechanical property

Tensile strength: 420 Mpa 60900 psi     Yield strength: 350 Mpa 50800 psi

Elongation at break (in 50 mm):0.29     Hardness, Brinell:121

Bebon International always uphold the purpose of mutual benefit, We always provide preferential prices and comprehensive services of AISI 1020 carbon steel tube. If you place an order of AISI 1020 steel tube to us, we will give you a satisfactory answer.

 

It is possible to process 1018 steel tube so as to get a combination of various characteristics of the likes of high tensile properties, superb micro-structure uniformity, good surface quality and excellent machinability. By the process of hot rolling SAE 1018 carbon steel, it is thus possible to make cold drawn seamless mechanical tubes. This type of tubing conforms to ASTM A519 standards. 1018 steel tubes are in big demand for use in a large number of mechanical applications as they have a smooth finish, they have close tolerances and they provide high yield strength.